Poly(silyl silane)homo and copolymers

ABSTRACT

Poly(silyl silanes) have been prepared. They have high photosensitivity and excellent resistance to oxygen-reactive ion etching processes. They are useful as photodepolymerizable photoresists, barrier layers, etc.

The U.S. Government has rights in this invention pursuant to ContractNo. DE-AC04-76DP00789 between the U.S. Department of Energy and AT&TTechnologies, Inc.

BACKGROUND OF THE INVENTION

This application relates to a new class of homo and copolymers havingproperties which make them especially useful as photoresists, especiallyin view of their very high resistance to oxygen reactive ion etching (O₂-RIE).

U.S. Pat. Nos. 4,587,205 and 4,588,801 to Zeigler et al describepolysilane polymers useful as self-developing photoresist materials, aswell as methods for their use in microlithography and other highresolution imaging applications. These are the pioneer patents in thepolysilane field. A major factor for the high level of interestgenerated by the inventions of these patents, in addition to theirself-developing capabilities, is the very high resistance to O₂ -RIE ofthe materials. They etch about 30 times slower than standardpositive-working photoresists under the same conditions.

O₂ -RIE resistance allows the combining in a single layer of thesematerials of the functions normally provided in two layers in trilayeror, more generally, multilayer lithography. Thus, a single layer ofself-developing polysilane can be used to combine the functions of theimaging layer and the etch barrier layer in conventional methods.Trilayer lithography can be converted as a result into bilayerlithography using the potential of the photovolatilizing polysilanes.This simplification allows the numbers of steps necessary to carry outmultilayer lithography to be cut essentially in half, with attendantreductions in cost and pollutant emissions and increases in deviceyield. As the topography of integrated circuits becomes even greater atsmaller critical device dimensions, multilayer lithographic schemesbecome increasingly necessary to print the submicron features present inthe state-of-the-art VLSI circuits. Thus, the importance ofself-developing polysilanes is proportionately increased.

The smallest feature that can be transferred to, e.g., a silicon waferby bilayer lithography is closely related to the ratio of the etch rateof underlying planarizing layer to that of the imaging layer; the higherthis ratio is, the smaller the feature printed in the imaging layer thatcan be transferred without unacceptable loss of feature resolution. Eventhough the polysilanes of the prior art have very high etch rate ratios,materials exhibiting even higher ratios are much desired.

SUMMARY OF THE INVENTION

It is, thus an object of this invention to provide a new class ofpolymers retaining or surpassing the properties of the known polysilanesand, especially, having high photosensitivity and permitting higher etchrate ratios in bilayer lithography.

Upon further study of the specification and appended claims, furtherobjects and advantages of this invention will become apparent to thoseskilled in the art.

These objects have been achieved by providing a new class of polymers,i.e., the poly(silyl silanes). These polymers have the structure ofpolysilanes having a main chain of catenated silicon atoms and pendantside groups, at least one of the latter being a silyl group.

The poly(silyl silanes) of this invention include those of the formula##STR1## wherein

each of A, B, C, D, E, F, . . . independently is silyl, e.g.,organosilyl, poly(silyl, e.g., organosilyl), organo or H,

at least one of A and B or A, B, C and D or A, B, C, D, E and F beingsilyl or polysilyl, e.g., organosilyl or poly(organosilyl).

In another aspect, this invention relates to a method of photopatterningan image onto a substrate coated with a photoresist which is apoly(silyl silane) homo- or copolymer comprising irradiating the coatedsubstrate with actinic radiation forming a pattern of said image on thesubstrate. As with the polysilanes of U.S. Pat. Nos. 4,587,205 and4,588,801, the image can be developed in the polymers of this inventionwithout use of a solvent development step. Under appropriatewavelength/fluence conditions, the poly(silyl silanes) of this inventionwill photodepolymerize and in may cases volatilize upon exposure toactinic radiation.

In yet another aspect, this invention provides, in a method of formingan image in a substrate comprising exposing a coated substrate tooxygen-reactive ion etching wherein the coating on the substrate is atleast ternary and comprises a planarizing layer, a barrier layer and aphotoresist layer, the improvement wherein said ternary portion isreplaced by a binary portion comprising a planarizing layer and a layerof a poly(silyl silane) which serves the function of both said barrierand photoresist layers.

In a further aspect, this invention relates to a process for preparing apoly(silyl silane) precursor R₁ R₂ R₃ Si-SiR₄ R₅ R₆ wherein R₁₋₅ arealiphatic or aromatic groups, and R₆ is an aromatic group, comprisingreacting R₄ R₅ R₆ SiCl with an alkali metal, M^(o), to form R₄ R₅ R₆ SiMand reacting the latter with ClSi R₁ R₂ R₃ to form R₁ R₂ R₃ Si-SiR₄ R₅R₆, wherein the latter reaction is carried out in situ with respect tothe first step.

Suitable silyl groups within the scope of this invention include allthose whereby the corresponding poly(silyl silanes) have utilitarianproperties, e.g., as photoresist layers for very high resolutionlithography or for very low resolution applications, e.g., whereindecorative patterns are to be incorporated onto or into a surface; as O₂-RIE resistant layers for use as simple etch barriers in multilayerlithography; as temporary coating layers for substrates, e.g., forprotective purposes, e.g., for transportation in the absence of actinicradiation, followed by coating removal by the convenientdepolymerization characteristics of the poly(silyl silanes) of thisinvention, e.g., upon exposure to actinic radiation; as photoinitiators;as curing agents; as photosensitizers; as highly thermally stable,non-charring encapsulants; as ceramic fiber precursors; as non-linearoptical materials; etc. Thus, all inorganic or organic silyl groupsproviding such polymers are included. Preferably, the silyl substituentsare organo, but may also be organosilyl.

Suitable organo groups on the silyl groups or on the main chain of thepolysilane portion of the polymers of this invention are also very broadin nature and will also be chosen to provide polymers having utilitarianproperties such as those discussed above.

Suitable organo groups include aliphatic and aromatic groups, typicallyhydrocarbon in nature, non-hydrocarbons also being suitable. The groupsmay be saturated or unsaturated, substituted or unsubstituted. Typicalnon-limiting examples of suitable organo groups include C₁₋₁₅ -alkyl, C₂-C₇ -alkylene, C₃₋₁₅ -cycloalkyl, C₆₋₁₄ aryl, C₇₋₂₀ -aralkyl or C₇₋₂₀-alkaryl. Organo groups in the side chain silyl groups also includeorganosilyl and poly(organosilyl). The alkyl portions in each of theorgano groups include, as appropriate, methyl, ethyl, n-propyl,i-propyl, n-butyl, i-butyl, sec-butyl, t-butyl, as well as any of thepentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, tridecyl,tetradecyl and pentadecyl groups. Suitable aryl portions include phenyl,naphthyl, etc. Suitable cycloalkyl groups include cyclopropyl,cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl, adamantyl,etc. Suitable arylalkyl groups include benzyl, phenethyl, phenylpropyl,etc.; suitable alkaryl groups include tolyl, xylyl, etc. Inorganicgroups are also included, e.g., R₂ B-groups where the R groups areorgano groups (e.g., preparable using fully conventional chemistryanalogous to the silicon chemistry described below, e.g., that of Scheme2, e.g., using Ph₂ BCl, etc.).

The organo groups can also be substituted, e.g., by C₁₋₈ -alkyl, C₁₋₈-alkoxy, C₆₋₁₀ -aryl, mono- or di(C₁₋₆ -alkyl)-amino, C₂₋₈ -alkanoyl ora corresponding ketal, amino, hydroxy, C₂₋₈ -alkanoyloxy, etc. As withthe organo groups per se, the nature of the substituents, if any, willnot be critical and will be determined by the polymer properties desiredfor a particular end use, inter alia. For example, where resistance tooxygen-reactive ion etching is desired, only substituents which providesufficient etch stability will be used.

Also included within the scope of organo groups of this invention areheterocyclic groups, e.g., aliphatic or aromatic heterocyclic groups of1-3 fused rings, each containing 4-7 ring atoms, 1-3 of which in eachring are O, N or S or even Si, the remainder being C-atoms. Suitableheterocyclic rings include morpholinyl, piperidinyl, pyridyl, etc. Forother suitable hetero groups see, e.g., copending application Ser. No.910,672, filed Sept. 23, 1986, now U.S. Pat. No. 4,761,464, which isentirely incorporated by reference herein.

Preferred organo groups include methyl, ethyl, n- or i-propyl, t-butyl,cyclohexyl, phenyl, phenyl-C₁₋₃ -alkyl, or C₁₋₃ -alkylphenyl.

The most preferred organo group on the silyl groups is methyl, e.g.,trimethylsilyl is a preferred silyl group. The silyl groups can also bebranched, i.e., substituents on the silyl groups include organo silylgroups or poly(organosilyl) groups. Thus, suitable silyl groups includeSi(R)(SiR₃)₂, where the R groups are organo groups, most preferablymethyl but also other silyl groups.

It is possible for all of A, B, C and D to be silyl or polysilyl groups.However, it is preferred that only one of A and B in homopolymers andonly one of A, B, C and D in copolymers be a silyl group. Theimprovement in photosensitivity and O₂ -RIE resistance provided by asingle silyl substituent in the recurring chain (vis-a-vis prior artpolysilanes) is very large. The relative effect of additional silylgroups is not as large and they usually make synthesis more difficult.

For the most important uses of this invention, the poly(silyl silanes)will be essentially oligomer free, e.g., by application of fullyconventional fractionation procedures, substantially non-crystalline,homogeneous, soluble, essentially linear, etc. in accordance with thedesired use. For the preferred uses of this invention, the polymers willalso be substantially not crosslinked, e.g., to facilitatephotodepolymerization.

The polymers of this invention typically have values of n of at least 10or 20, preferably of at least 30, 40, 50, 100, 500, 1000, 10000, etc.The lower value of n will be use-dictated, e.g., to achieve theforegoing properties, e.g., essentially oligomer-free and to providegood film forming ability, etc.

Where a silyl side group comprises oligo- or poly(silyl silane)moieties, the length of the side chain is preferably no more than aboutone-half the length of the main chain. Longer side chains tend toproduce polymer solutions which are highly viscous or even gelatinousand thus which fail to satisfy the stringent requirements of the highresolution photolithographic uses of this invention. Thus, at the lowerend of the preferred range of values of n, e.g., typically 25-30, thedegree of polymerization in the side chains will not be greater thanabout 13-15. This side chain length requirement is not as important forthe less demanding uses of the poly(silyl silanes), e.g., merely asprotective coatings. The upper limit on n is determined only by theparticular conditions utilized in the preparative process for a givenpolymer, e.g., often at very high values of n, a polymerization mediumand solutions prepared from the isolated polymers will become tooviscous for effective handling. Typically, molecular weights up to10,000,000 or more can conveniently be prepared and utilized.

As discussed thoroughly in U.S. Pat. Nos. 4,587,205 and 4,588,801, bothof which are entirely incorporated by reference herein, wherephotovolatilization characteristics are desired in a polysilane-typepolymer, it is necessary that the polymer have sufficientphotosensitivity to form fragments upon exposure to actinic radiationand that these fragments be of sufficiently low molecular weight to bevolatile under the irradiation conditions. For the polysilanes of theprior art, this balance necessarily had to be struck rather delicately.A significant advantage of the poly(silyl silanes) of this invention isthat the balance is much less critical. The mere existence of pendantsilyl groups essentially ensures that the polymer will have the highphotosensitivity needed to form fragments upon irradiation. Achievementof the necessarily low fragment weight can routinely be accomplished,perhaps with a few preliminary orientation experiments, for a givenpolymer system by appropriate choice of organo substituents on the silylgroups. Where the latter are oligo- or poly(silyl) groups, achievementof the necessary low fragment weight will be greatly facilitated byscission in the side chains per se. Moreover, scission of the silyl mainchain Si--Si bond will also achieve this function.

In the past, this need for low weight fragments was somewhatinconsistent with the need for bulky side groups which increasedphotosensitivity. Here, not only are the pendant silyl groups by andlarge bulky, but, more importantly and surprisingly, they additionallysignificantly increase the photochemical sensitivity of the polymer,e.g., in comparison with prior art polysilanes. It is believed, withoutwishing to be bound by theory, that this is a result of their catalysisof intersystem crossing to the photochemically active triplet state.

The preferred use of the poly(silyl silanes) of this invention is inphotolithography. Like the prior art polysilanes, the homo- andcopolymers of this invention can be used as conventional photoresists,albeit ones having high photosensitivity and excellent resistance tooxygen-reactive ion etching. Thus, they can be photopatterned usingactinic radiation fully in accordance with prior art methods. Ifdesired, the photoresists can be developed using solvents which dissolvethe exposed portions of the polymer (photodepolymerized and notvolatilized) but not the unexposed portions. Typical such solventsinclude lower alkanols such as isopropyl alcohol, ethyl acetate, up toC₇ alkanes and mixtures of these with solvents for the polymers. Moreoften, development will be solvent-free, taking advantage of thephotovolatilization phenomenon described in the foregoing references.

Where desired, conventional solvent stripping methods can be utilized toremove the poly(silyl silane) photoresists after the substrate treatmentsteps. Again, taking maximum advantage of this invention, this strippingstep can also be accomplished in solvent-free fashion by simply exposingthe entire surface to high flux actinic radiation which will cause theentire remaining amount of poly(silyl silane) to photovolatilize.

The self-developing polysilanes of U.S. Pat. Nos. 4,588,801 and4,587,205 and Zeigler et al, SPIE, 539, 166 (1985), also incorporatedentirely by reference herein, exhibit highly efficient photochemistrydespite the fact that their singlet excited states fluoresce in a narrowhigh quantum yield (φ_(f) =0.45-0.7) emission characteristic of adelocalized excited state. This phosphorescence, on the other hand,shows strong vibrational coupling, suggestive of a localized excitation,and is of exceedingly low quantum yield (φ_(p) ˜10⁻⁴). It is thuspostulated (without wishing to be bound by theory) that the tripletstate is responsible for prior art polysilane solid-statephotochemistry. The so-called "heavy atom effect" on intersystemcrossing to the triplet manifold, it is believed without wishing to bebound by theory, at least partially causes the poly(silyl silanes) tohave much lower fluorescence and increased photosensitivity over theprevious materials. It has how been found that the fluorescence of thepolymers, e.g., poly(trimethylsilyl methyl silane) is present not as asingle band as in the previous polysilanes, but is doubled and has φ_(f)≃0.02 (an approximately 20-30 fold reduction over previous polysilanes).Moreover, a 1:1 copolymer of the trimethylsilyl MeSi subunit withcyclohexyl MeSi is approximately four times as photosensitive in theself-developed mode as (cyclohexyl MeSi)_(n). This gives an approximatesensitivity of 200 mJ/cm² /1μ thickness (cf. 150 mJ/cm² /1μ of standardsolvent developed positive resist and about 800 mJ/cm² /1μ of prior artpolysilanes).

Further advantageously, the increased content of silicon atoms in thepolymers of this invention causes them to have etch-rate ratios whichare significantly higher than those previously available in polysilanes.See, e.g., Taylor et al, Solid State Tech., 145 (2/84). In prior artpolysilanes, the highest silicon-content member which is air stable is(Me₂ Si)_(n) which, unfortunately, is intractable and cannot be used asa resist. One of the simplest polymers of this invention,poly(trimethylsilyl methyl silane), has the same silicon content as (Me₂Si)_(n) but is fully soluble. In comparison with etch rate ratios ofabout 30:1 for prior art self-developing polysilanes, etch rate ratiosof the polymers of this invention are significantly higher, e.g., 50:1and more. Because of this property, the polymers of this invention areespecially useful as oxygen-reactive ion etch resistant layers. Forexample, they can be utilized as barrier layers in the conventionaloxygen-reactive ion etch processes. More preferably, they can beutilized to serve the function as both the barrier layer and thephotoresist layer. In this regard, see U.S. Pat. No. 4,464,460 and JPNo. 60,119,550 (Chem. Abstracts 103 132441z (1985), whose disclosuresare entirely incorporated by reference herein. Thus, the polymers ofthis invention will be of wide applicability in all areas where suchetching processes are utilized.

In yet another application, the poly(silyl silanes) of this inventioncan be used as photosensitizers or photoinitiators in mixtures ofphotopolymerizable vinyl monomers or prepolymers, e.g., in accordancewith the details of U.S. Pat. No. 4,569,953, which is entirelyincorporated by reference herein.

For all the foregoing uses, the polymers of this invention can be usedsubstantially analogously to the corresponding use of the polysilanes inthe past. However, advantage can be taken of the increasedphotosensitivity of the polymers of this invention, e.g., lower fluxeswill be available for photovolatilization modes. The actinic radiationwavelength range is essentially the same as that for prior artpolysilanes, i.e., in the ultraviolet wavelength range.

The poly(silyl silanes) of this invention can be prepared usingconventional silicon chemistry except as indicated otherwise below.

For example, the following 2-step reaction can be employed asexemplified for Me₃ Si--MeCl₂ : ##STR2##

The first two steps as practiced by this invention constitute aconsiderable process simplification over the prior art in that thecoupling of Ph₂ MeSiCl to form Ph₂ MeSiSiMePh₂ and reductive cleavage toPh₂ MeSiLi followed by reaction with trimethylsilylchloride areperformed in a 1-pot reaction. The first step is generally conducted attemperatures of -50° to 100° C. (preferably 20°-25° C.) for reactiontimes in the range of about 20 minutes to about 24 hours. Typically,from about 1.7 to about 4 equivalents of lithium (or another alkalimetal, e.g., Na^(o) or K^(o)) are utilized. Suitable solvents includetetrahydrofuran, glyme, ether and other equivalents. This first steptypically achieves about a 70% conversion in the presence ofstoichiometric lithium.

After completion of the first step an in situ coupling to form theSi--Si bond is achieved simply by titration-like addition of anessentially stoichiometric amount of Me₃ SiCl. During this reaction,completion can be easily detected by loss of the inherent dark red colorof Ph₂ MeSiLi. The reaction is essentially instantaneous, silaneaddition typically being completed in less than about an hour. Reactiontemperature is non-critical and simply must be less than the boilingpoint of the silane added and the decomposition point of Ph₂ MeSiLi.Typically, the reaction is conducted at 25°-50° C.

Upon completion of the second step, the reaction medium can be stirredin the presence of the excess lithium whereupon the remaining Ph₂MeSi--SiMePh₂ will be converted to the corresponding lithium compoundagain to an extent of about 70%. The cycle can then be repeated adesired number of times to significantly increase the overallconversion. The final step of the process, cleaveage of the phenylgroups with HCl, is conducted in accordance with the procedures ofIshikawa et al, J. Organomet. Chem. 118, 151 (1976), whose disclosure isentirely incorporated by reference herein.

This basic scheme can be used to prepare a wide variety of the monomersneeded to prepare the poly(silyl silanes) of this invention. Forexample, the various methyl groups in the starting materials can bereplaced by essentially any of the organo groups mention above exceptfor aryl and substituted aryl groups and other groups which do notsurvive the Scheme 1 reactions, e.g., bulky groups like t-butyl, groupshaving O or N bonded directly to Si like alkoxy, morpholine, etc. Incases of doubt, routine preliminary experiments can be performed todetermine the suitability of the foregoing reaction chemistry to thepreparation of the monomer of interest.

Where the foregoing chemistry is not applicable, other conventionaltechniques can be utilized. For example, where it is desired to couple asilane having an aryl group to another silane, e.g., SiMe₃ Cl, thechemistry of Scheme 2 can be utilized: ##STR3##

This reaction is also a general one, involving conventionalhalogen-metal interchange with an appropriate organolithium reagent or,alternatively, conventional Grignard reagent formation from the arylhalide, to prepare the corresponding arylorganometallic compound. Thelatter can be conventionally reacted with, e.g., tetrachlorosilane toafford ArSiCl₃. Conventional treatment of the latter with a respect suchas Me₃ SiK yields the desired monomer. Suitable aryl groups includephenyl, naphthyl, substituted aryl and the other aryl moieties mentionedabove. X is halo, including Cl, Br, I, F. The coupling step can beachieved with a wide variety of R₃ SiK or R₃ SiLi reagents to afford awide variety of aryl-containing monomers.

Similarly, the chemistry of Scheme 2 can also be used where Ar isreplaced by another organo group from among those described above.Suitable such groups will include the foregoing organo groups except forthose which are incompatible with lithium reagent formation, e.g.,ketone functionalities, etc.

Where Ar is replaced by, e.g., n-alkyl, the trichlorosilane (analogousto ArSiCl₃ in the foregoing) can be prepared by conventionalhydrosilation of the corresponding alkene, for instance, with HSiCl₃ inthe presence of a noble metal catalyst (e.g., chloroplatinic acid) togive, e.g., the corresponding n-alkyl SiCl₃ compound. The trihalosilanecan then be converted to the appropriate silylated monomer as shown inScheme 2. The Grignard or lithium reagent chemistry shown in Scheme 2 inconjunction with aryl groups is preferred where branched alkyl groupsare involved.

The foregoing chemistry can be combined in many self-evident ways toprepare a wide variety of the monomers necessary to prepare desiredpoly(silyl silanes).

Where the side chains involve silyl groups having more than one siliconatom, other conventional chemistry can be utilized. For example, wherethe number of silicon atoms in the side group is 3-7, the chemistry ofScheme 3 will be appropriate: ##STR4##

The ring compounds shown as starting materials are commerciallyavailable or otherwise readily available by conventional coupling ofdihalosilanes using lithium or magnesium. (In the latter reactions, theresultant predominant ring size varies with the nature of thesubstituent, bulky substituents tending to give smaller ringspreferentially.) The ring opening reaction shown above to prepare theα,ω-dihalooligosilane is a very facile one. It can be performed in thesame pot as the subsequent reaction with RLi to give the corresponding1-halooligosilane. Reaction of the latter with R₁ R₂ R₃ SiM, e.g., MePh₂SiLi as described above, followed by cleavage of the phenyl groups withHCl/AlCl₃, can be used to attach the oligosilyl group to a wide varietyof SiR₃ groups as described above. R₁, R₂, R₃ are organo groupsdiscussed above, at least one being cleavable, e.g., phenyl, alkoxy,etc., as described above. Similarly, other known coupling reactions(described in the literature or herein) can be utilized to form thedesired monomer.

Larger oligosilane side groups can be prepared, e.g., using thechemistry of Scheme 4: ##STR5##

In essence, the methodology involves the dimerization, oligomerization,or even polymerization of the multiple Si-containing silanes discussedabove (where R₁ and R₂ are organo as described herein), e.g., usingmethods analogous to those of Boberski et al, J. Organomet. Chem. 88, 65(1975), which disclosure is entirely incorporated by reference herein.For example, as shown above, to obtain a Si₁₄ side chain a1-halo-7-arylheptasilane produced, e.g., in accordance with Scheme 3above, where R is aryl, can be reductively coupled with a1-halo-7-alkyl-heptasilane using lithium or sodium metal. Extrapolationsto other combinations are apparent. The coupling product is then treatedwith HCl to give a corresponding 1-chloro-tetradecasilane. The latter isthen utilized in the chemistry of Scheme 3 (or Scheme 1) to afford,ultimately, the desired 1,3-dichloro-pentadecasilane.

Side chains having two or three silicon atoms can be prepared usingdisilane or trisilane monomers which are commercially available or whichcan fully conventionally be prepared using coupling reactions such asthose described above.

In general, details of all of the mentioned conventional reactions willbe routinely chosen in accordance with conventional considerations,perhaps in conjunction with a few routine preliminary experiments, andwith reference to well known publications in the field, e.g.,Organosilicon Compounds, Victor Bezant et al, Academic Press, N.Y.(1965); I. Fleming, "Organic Silicon Chemistry", Comprehensive OrganicChemistry, Ch. 13, Vol. 2, Pergamon (1979); E. Hengge, Topics in CurrentChemistry, Vol. 51, Springer Verlag, Berlin (1974), all of whosedisclosures are entirely incorporated by reference herein.

Once the monomers are obtained, they can be polymerized to afford thedesired poly(silyl silane) using fully conventional reaction chemistrydescribed in the various references cited and/or incorporated byreference above by the procedures described in U.S. Ser. No. 851,713 ofApr. 13, 1986. The primary polymerization technique is reductivecoupling using sodium metal. As usual, the monomers and solventsutilized in this reaction must be rigorously pure in order to achievethe most useful molecular weights and yield. Thus, they must beessentially free of typical impurities such as siloxanes,trichlorosilanes, HCl, etc. The necessary purities are availablecommercially where the corresponding reagent is available commercially.The necessary purities can be routinely achieved applying conventionalpurification procedures where necessary.

The most preferred methods for preparing the polymers of this inventionare those utilizing the optimum solvent mixtures arrived at byprocedures in accordance with U.S. patent application No. 851,713, filedApr. 13, 1986, whose disclosure is entirely incorporated by referenceherein. In this regard, for synthesis of the poly(silyl silanes) of thisinvention, it has been found to be advantageous to use slower sodiumdispersion addition rates than those described in the mentionedapplication, e.g., rates which are considerably less than those normallyemployed for preparation of the conventional polysilanes, e.g., 10-100meq/min versus 320 meq/min.

The poly(silyl silane) homo and copolymers of this invention are solublein a wide variety of non-polar solvents, (e.g., toluene, xylene,heptane, decane, tetrahydrofuran, etc.). Films can be cast from thecorresponding solutions. Solvent casting, spin casting, dipping,spraying, etc., are all applicable film-forming techniques. A widevariety of substrates can be coated with the poly(silyl silanes) of thisinvention, e.g., all of those useful in conjunction with the prior artpolysilanes. Good adhesion is observed. Of course, substrates useful inmicroelectronic design are especially preferred, e.g., silicon,aluminum, semiconductors, quartz, sapphire, etc.

Without further elaboration, it is believed that one skilled in the artcan, using the preceding description, utilize the present invention toits fullest extent. The following preferred specific embodiments are,therefore, to be construed as merely illustrative, and not limitative ofthe remainder of the disclosure in any way whatsoever.

In the preceding text and the following examples, all temperatures areset forth uncorrected in degrees Celsius and all parts and percentagesare by weight; unless otherwise indicated.

EXAMPLE 1 Synthesis of Ph₂ MeSi--SiMe₃

A slurry 89.3 g of Li metal cut into small pieces in 1500 ml drytetrahydrofuran (THF) under an Ar atmosphere was treated dropwise withneat Ph₂ MeSiCl (1302.2 g, 5.59 moles). During the addition, agitationwas provided via a mechanical stirrer and an ice bath was employed asnecessary to hold the reaction temperature under 40° C. The mixture wasthen allowed to stir overnight (16 hr.) at room temperature. The darkred solution of Ph₂ MeSiLi was then treated with 607.7 g (5.59 moles) ofMe₃ SiCl dissolved in 700 ml dry THF. Again an ice bath was utilized tomaintain the reaction mixture temperature under 40° C. Near the end ofthe Me₃ SiCl addition, the red color of Ph₂ MeSiLi was completelydischarged. Upon completion of the addition, the now essentiallycolorless mixture was filtered to remove precipitated LiCl and unreactedLi metal. Solvent was removed from the resulting clear solution atreduced pressure and the residual oil fractionally distilled at 0.3 mmHg to afford 1074.1 g of title compound (71%), bp 108°-110° C.

EXAMPLE 2 Synthesis of Me₃ Si--SiMeCl₂

Ph₂ MeSi--SiMe₃ (1074.1 g) prepared as in Example 1 was reacted in drybenzene solution with gaseous HCl in the presence of 6 g anhydrous AlCl₃catalyst essentially according to the procedure of Ishikawa et al (J.Organomet. Chem., 118, 151 (1976)). Distillation of the crude product as80 mm Hg afforded 473.5 g (64%) of product, bp. 78° C.

EXAMPLE 3 Preparation of (TrimethylsilylMeSi)_(n)

A solution of 4.9 g (26.2 mmole) of Me₃ Si--SiMeCl₂ in a mixture of 65ml dry toluene and 35 ml dry heptane was heated to reflux and 3.31 g of40% Na dispersion in mineral spirits added at a rate of 80 meq/min. Thedark blue reaction mixture was heated at reflux for 1 hour aftercompletion of the addition, then allowed to cool to room temperature. Itwas quenched by addition of about 5 ml methanol followed by 100 ml ofsaturated aqueous NaHCO₃ solution. The colorless reaction mixture thusobtained was filtered through diatomaceous earth and the organic phaseseparated. This was then stripped of solvent and the oily producttreated with 50 ml ethyl acetate to precipitate the polymer. Afterfurther precipitations from toluene solution with ethyl acetate andtetrahydrofuran solution with methanol, 40 mg of the title polymer wasobtained. Size exclusion chromatography gave an M_(w) of 359000 for thismaterial (relative to polystyrene standards). IR (KBr wafer) (cm⁻¹):1260(Si--Me), 1250--(Si--Me₃), 845(Si--Me₃), 758(Si--Me₃), 785(Si--Me).

EXAMPLE 4 Preparation of (Me₃ Si--SiMe/PhMeSi)_(n)

A mixture of 10.21 g (53.4 mmol) PhMeSiCl₂ and 10 g Me₃ Si--SiMeCl₂(53.4 mmol) was polymerized in a mixed solvent composed of 54 ml tolueneand 46 ml heptane in a manner exactly analogous to that used in Example3. After workup as in Example 3 and precipitations using hexanes inplace of the ethyl acetate used in the previous example, 0.54 g of thetitle copolymer was isolated. An M_(w) of 160000 was found by sizeexclusion chromatography (relative to polystyrene standards). IR (KBrwafer): 1440 (Si--Ph), 1260 (Si--Me), 1250 (Si--Me₃), 845 (SiMe₃), 835(Ph--H bend), 625 (Ph--H bend). ¹ H NMR (CDCl₃) (δ): -0.5 (br. s.,Si--CH₃), 7.1 (br. s., Si--Ph). Integration of the Si--Ph absorptionrelative to the Si--CH₃ absorption indicated a 65:35 ratio of PhMeSi toMe₃ Si--SiMe subunits, respectively.

EXAMPLE 5 Preparation of (Cyclohexyl MeSi/Me₃ Si--SiMe)_(n)

A refluxing solution of 154 g (0.781 mol) cyclohexylmethyldichlorosilaneand 146.2 g (0.781 mol) 1,1-dichlorotetramethyldisilane in a mixture of396 ml toluene and 504 ml heptane was reacted with 263.3 g of 30% Nadispersion in toluene added at the most rapid rate allowed by theexothermic reaction. The resulting mixture was allowed to reflux for 50min after completion of the addition, then allowed to cool for 16 hoursto ambient temperature. After workup and purification identical to thatused in Example 1, 2.17 g of the title polymer was obtained having M_(w)of 164000 by SEC. IR (KBr) (cm⁻¹): 1260 (SiMe₃), 1250 (Si--Me), 1040(CH₂ bend), 2915 (C--H stretch). ¹ H NMR (CDCl₃): δ0.2 (br.m., Si--CH₃),1.3 (br.s., cyclohexyl H), 2.3 (br.s., cyclohexyl H).

EXAMPLE 6 Preparation of (n-Propyl MeSi/Me₃ Si--SiMe)_(n) by "Normal"Addition Mode

A slurry of 33.8 g 40% Na dispersion in mineral oil in a refluxingmixture of 4 ml toluene and 42 mol heptane was reacted dropwise at 320meq/min with a 50% v/v solution of 25 g (133.5 mmol) of Me₃ Si--SiMeCl₂and 21.0 g of n-propylmethyldichlorosilane in the same solvent mixture.The reaction was completed as in Example 5 and the product polymerisolated in the same fashion to afford 1.41 g of the title polymer as arubbery solid. A molecular weight, M_(w), of 19000 was found by SECrelative to polystyrene standards.

EXAMPLE 7 Preparation of (Me₂ Si/Me₃ Si--SiMe)_(n)

A solution of 6.20 g (48.1 mmol) dimethyldichlorosilane and 9.0 g (48.1mmol) 1,1-dichlorotetramethyldisilane were reacted with 12.16 g 40% Nadispersion in light oil in a mixture of 69 ml n-decane and 31 ml tolueneas in Example 3. After an identical workup and product purificationprocedure, 120 mg of pure white solid title polymer was obtained. TheM_(w) of this material was 33000. Infrared and H NMR spectroscopic dataconsistent with the assigned structure were obtained.

EXAMPLE 8 Preparation of (Isopropyl MeSi/Me₃ Si--SiMe)_(n)

A mixture of 4.2 g (26.7 mmol) isopropylmethyldichlorosilane and 5 g(26.7 mmol) of 1,1-dichlorotetramethyldisilane were reacted with Nadispersion (6.75 g of 40% Na in light oil) in a reaction solvent of 50ml toluene and 50 ml decane according to the procedure given in Example3. 28 mg of pure white polymer with M_(w) =65000 were obtained. IR (KBrwafer) (cm⁻¹): 1385, 1368(C--(CH₃)₂), 1250 (Si--Me₃), 750 (Si--Me₃), 779(Si--Me₃).

EXAMPLE 9

Analogously to Example 3, using the corresponding monomers and usingsolvent systems calculated in accordance with U.S. Ser. No. 851,713 ofApr. 13, 1986, the following copolymers are prepared having therecurring unit --Si(A)(B)Si(C)(D)--, wherein A and C are methyl, and foreach of B=cyclohexyl, t-butyl, i-propyl or n-propyl, D=trimethylsilyl,triphenylsilyl or triethylsilyl.

The preceding examples can be repeated with similar success bysubstituting the generically or specifically described reactants and/oroperating conditions of this invention for those used in the precedingexamples.

From the foregoing description, one skilled in the art can easilyascertain the essential characteristics of this invention, and withoutdeparting from the spirit and scope thereof, can make various changesand modifications of the invention to adapt it to various usages andconditions.

What is claimed is:
 1. In a linear polysilane having a main chain of atleast ten catenated Si atoms and pendant side groups, the improvementwherein at least one side group is a silyl group.
 2. A linear poly(silylsilane) having at least ten recurring units.
 3. A poly(silyl silane) ofclaim 2 of the formula ##STR6## wherein each of A, B, C, D, E and Findependently is organosilyl, poly(organosilyl), organo or H,at leastone of A, B, C, D, E and F being organosilyl or poly(organosilyl).
 4. Apolymer of claim 3 of the formula ##STR7##
 5. A polymer of claim 3 ofthe formula ##STR8##
 6. A polymer of claim 3, wherein the chain lengthof side chain poly(organosilyl) groups is up to about one-half the chainlength of the main chain.
 7. A polymer of claim 3, wherein none of A, B,C, D, E and F is H.
 8. A polymer of claim 3, wherein all of A, B, C, D,E and F are organosilyl or poly(organosilyl).
 9. A polymer of claim 3,wherein only one of A, B, C, D, E and F is silyl or poly(organosilyl).10. A polymer of claim 3, wherein at least two of A, C and E are silylor poly(organosilyl).
 11. A polymer of claim 3, wherein the organoportions are aliphatic or aromatic groups wherein said polymer isresistive to oxygen-reactive ion etching.
 12. A polymer of claim 3,wherein the organo groups are C₁₋₁₅ -alkyl, C₃₋₁₅ -cycloalkyl, C₆₋₁₄-aryl, C₇₋₂₀ -aralkyl or C₇₋₂₀ -alkaryl and those in the side chainsilyl groups can also be organosilyl or poly(organosilyl) and n is atleast 30, or C₂₋₇ -alkylene.
 13. A polymer of claim 7, wherein theorgano groups are C₁₋₁₅ -alkyl, C₃₋₁₅ -cycloalkyl, C₆₋₁₄ -aryl, C₇₋₂₀-aralkyl or C₇₋₂₀ -alkaryl and those in the side chain silyl groups canalso be organosilyl or poly(organosilyl) and n is at least 30, or C₂₋₇-alkylene.
 14. A polymer of claim 13, wherein the organic portions aremethyl, ethyl, n- or i-propyl, t-butyl, cyclohexyl, phenyl, phenyl-C₁₋₃-alkyl or C₁₋₃ -alkylphenyl.
 15. A polymer of claim 13, wherein thesilyl groups are trimethylsilyl groups.
 16. A polymer of claim 13,wherein said organo groups are substituted by C₁₋₈ -alkyl, C₁₋₈ -alkoxy,C₆₋₁₀ -aryl, mono- or di(C₁₋₆ -alkyl)-amino, C₂₋₈ -alkanoyl, amino,hydroxy or C₂₋₈ -alkanoyloxy.
 17. A polymer of claim 14, wherein onlyone side group of the polymer's repeating unit is silyl.
 18. A polymerof claim 16, wherein only one side group of the polymer's repeating unitis silyl.
 19. A copoly(silyl silane) of claim 3 of the formula ##STR9##wherein B and D are methyl and A and C are cyclohexyl/trimethylsilyl,t-butyl/trimethysilyl, i-propyl/trimethylsilyl orn-propyl/trimethylsilyl and n is at least
 30. 20. A copoly(silyl silane)of claim 3 of the formula ##STR10## wherein B and D are methyl and A andC are cyclohexyl/triphenylsilyl, t-butyl/triphenylsilyl,i-propyl/triphenylsilyl or n-propyl/triphenylsilyl and n is at least 30.21. A copoly(silyl silane) of claim 3 of the formula ##STR11## wherein Band D are methyl and A and C are cyclohexyl/triethylsilyl,t-butyl/triethylsilyl, i-propyl/triethylsilyl or n-propyl/triethylsilyland n is at least
 30. 22. A poly(silylsilane) of claim 2 in isolatedform.
 23. A poly(silylsilane) of claim 2 which is essentiallyoligomer-free.
 24. A poly(silylsilane) of claim 2 which is substantiallynon-crystalline.
 25. A poly(silylsilane) of claim 2 which is soluble innon-polar solvents.
 26. A poly(silylsilane) of claim 2 which issubstantially not crosslinked.
 27. A poly(silylsilane) of claim 2wherein n is at least
 500. 28. A poly(silylsilane) of claim 2 wherein nis at least 1,000.
 29. In a solid, linear polysilane having a main chainof at least ten catenated Si atoms and pendant side groups, theimprovement wherein at least one side group is a silyl group.
 30. Asolid, linear poly(silyl silane) having at least ten recurring units.31. A solid, linear poly(silyl silane) of claim 30 of the formula##STR12## wherein each of A, B, C, D, E and F independently isorganosilyl, poly(organosilyl), organo or H,at least one of A, B, C, D,E and F being organosilyl or poly(organosilyl), and n is at least 10.